Non-halogen flame-retardant material with high heat resistance that can be applied to battery charger

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
V-2
UL94
mm
0,75
Flammability
V-0
UL94
mm
1.5,3.0
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,18
Melt Flow Index
250°C,10kg
ISO 1133
g/10min
19
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
121
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
135
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
123
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
135
Vicat Softening Temperature
B/50
ISO R 306
°C
140
Vicat Softening Temperature
B/120
ISO R 306
°C
145
RTI, Ele
1.5 ,V-0
UL746B
°C
130
RTI, Imp
1.5 ,V-0
UL746B
°C
130
RTI, Str
1.5 ,V-0
UL746B
°C
130
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
55
Tensile Strain at Break
50mm/min
ISO 527
%
109
Tensile Modulus
50mm/min
ISO 527
MPa
2100
Tensile Strength at Break
50mm/min
ISO 527
MPa
67
Flexural Strength
2mm/min
ISO 178
MPa
80
Flexural Modulus
2mm/min
ISO 178
MPa
2100
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
65
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
70
Rockwell Hardness
R-scale
ISO 2039-2
-
120