Starex SR-0330M

Telefonische Beratung

+49 40 727702-0

ABS

Properties
Test condition
Method
Unit
Value
Appearance
Yellowness Index
3,2mm
ASTM D1925
-
31,2
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,07
Melt Flow Index
220°C, 10kg
ISO 1133
g/10min
3
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,6
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,64
Melt Flow Index
250°C, 2,16kg
ISO 1133
g/10min
2
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
96
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
112
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
103
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
112
Vicat Softening Temperature
B/50
ISO R 306
°C
118
Vicat Softening Temperature
B/120
ISO R 306
°C
119
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
48
Tensile Strain at Break
50mm/min
ISO 527
%
15
Tensile Modulus
50mm/min
ISO 527
MPa
2330
Tensile Strength at Break
50mm/min
ISO 527
MPa
45
Flexural Strength
2mm/min
ISO 178
MPa
78
Flexural Modulus
2mm/min
ISO 178
MPa
2350
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
14
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
15
Rockwell Hardness
R-scale
ISO 2039-2
-
113
Izod Impact Strength (notched)
-30°C, 4mm
ISO 180 1A
KJ/m²
9
Charpy Impact Strength (V-notched)
At -30°C, 4mm
ISO 179 1eA
KJ/m²
10