Flame -retardant ABS material with the characte ristic of high he at

resistance that can be applied to battery case and adaptor

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
V-0
UL94
mm
1.5, 2.5-2.7
Flammability
5VB
UL94
mm
2.5-2.7
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,16
Melt Flow Index
200°C, 5kg
ISO 1133
g/10min
1,6
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,40~0,49
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,43~0,53
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
79
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
92
Vicat Softening Temperature
B/50
ISO R 306
°C
97
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
49
Tensile Strain at Break
50mm/min
ISO 527
%
9
Tensile Modulus
50mm/min
ISO 527
MPa
2300
Tensile Strength at Break
50mm/min
ISO 527
MPa
36
Flexural Strength
2mm/min
ISO 178
MPa
78
Flexural Modulus
2mm/min
ISO 178
MPa
2600
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
18
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
18
Rockwell Hardness
R-scale
ISO 2039-2
-
109