Starex VH-0800

Telefonische Beratung

+49 40 727702-0

Flame -retardant ABS material with the characteristic of high flow that can applied to the exterior material of OA de vice s such as monitor,

printer, fax machine , duplicator e tc.

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
V-0
UL94
mm
1.5, 3.0, 6.0
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,17
Melt Flow Index
200°C, 5kg
ISO 1133
g/10min
5,4
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,30~0,37
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,33~0,40
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
71
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
81
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
80
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
85
Vicat Softening Temperature
B/50
ISO R 306
°C
86
Vicat Softening Temperature
B/120
ISO R 306
°C
89
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
46
Tensile Strain at Break
50mm/min
ISO 527
%
8
Tensile Modulus
50mm/min
ISO 527
MPa
2400
Tensile Strength at Break
50mm/min
ISO 527
MPa
35
Flexural Strength
2mm/min
ISO 178
MPa
75
Flexural Modulus
2mm/min
ISO 178
MPa
2700
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
21
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
20
Rockwell Hardness
R-scale
ISO 2039-2
-
107