Starex VH-0819

Telefonische Beratung

+49 40 727702-0

Flame -r tardant ABS material with the characte ristic of high flow that can be used for the exterior material of large TV and OA devices

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
V-0
UL94
mm
2.1-2.3, 3.0
Flammability
5VB
UL94
mm
3
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,16
Melt Flow Index
200°C, 5kg
ISO 1133
g/10min
8
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
70
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
79
Vicat Softening Temperature
B/50
ISO R 306
°C
85
Vicat Softening Temperature
B/120
ISO R 306
°C
87
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
42
Tensile Strain at Break
50mm/min
ISO 527
%
10
Tensile Modulus
50mm/min
ISO 527
MPa
2200
Tensile Strength at Break
50mm/min
ISO 527
MPa
32
Flexural Strength
2mm/min
ISO 178
MPa
67
Flexural Modulus
2mm/min
ISO 178
MPa
2300
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
22
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
25
Rockwell Hardness
R-scale
ISO 2039-2
-
105