Starex WR-9120

Telefonische Beratung

+49 40 727702-0

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
HB
UL94
mm
1,5
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,06
Melt Flow Index
220°C, 10kg
ISO 1133
g/10min
17
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,40~0,49
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,42~0,52
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
72
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
90
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
95
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
99
Vicat Softening Temperature
B/50
ISO R 306
°C
98
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
47
Tensile Strain at Break
50mm/min
ISO 527
%
18
Tensile Modulus
50mm/min
ISO 527
MPa
2200
Tensile Strength at Break
50mm/min
ISO 527
MPa
34
Flexural Strength
2mm/min
ISO 178
MPa
67
Flexural Modulus
2mm/min
ISO 178
MPa
2100
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
11
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
16
Rockwell Hardness
R-scale
ISO 2039-2
-
106