Starex WR-9300HF

Telefonische Beratung

+49 40 727702-0

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
HB
UL94
mm
1,5
Appearance
Yellowness Index
3,2mm
ASTM D1925
-
25
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,07
Melt Flow Index
220°C, 10kg
ISO 1133
g/10min
12
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,22
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,26
Melt Flow Index
250°C, 2,16kg
ISO 1133
g/10min
6,5
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
80
Vicat Softening Temperature
B/50
ISO R 306
°C
100
Mechanical
Flexural Strength
2mm/min
ISO 178
MPa
67
Flexural Modulus
2mm/min
ISO 178
MPa
2100
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
12,1
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
14
Rockwell Hardness
R-scale
ISO 2039-2
-
106
Izod Impact Strength (notched)
-30°C, 4mm
ISO 180 1A
KJ/m²
5,4
Tensile Strength at Yield
5mm/min
ISO 527
MPa
44