Infino TN-1100

Telefonische Beratung

+49 40 727702-0

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
V-0
UL94
mm
2,5
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,23
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0.49-0.6
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0.51-0.62
Melt Flow Index
250°C,10kg
ISO 1133
g/10min
75
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
91
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
100
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
99
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
102
Vicat Softening Temperature
B/50
ISO R 306
°C
106
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
73
Tensile Strain at Break
50mm/min
ISO 527
%
87
Tensile Modulus
50mm/min
ISO 527
MPa
2400
Tensile Strength at Break
50mm/min
ISO 527
MPa
62
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
4,5
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
5
Rockwell Hardness
R-scale
ISO 2039-2
-
123
Flexural Strength
2,8mm/min
ISO 178
MPa
108
Flexural Modulus
2,8mm/min
ISO 178
MPa
2650