Infino WP-1098

Telefonische Beratung

+49 40 727702-0

Properties
Test condition
Method
Unit
Value
Appearance
Gloss
at 23°C, 50% RH, 60°
ISO 2813
%
35
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,13
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,5
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,7
Melt Flow Index
250°C,10kg
ISO 1133
g/10min
30
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
97
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
106
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
111
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
122
Vicat Softening Temperature
B/50
ISO R 306
°C
120
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
50
Tensile Strain at Break
50mm/min
ISO 527
%
100
Tensile Modulus
50mm/min
ISO 527
MPa
1700
Tensile Strength at Break
50mm/min
ISO 527
MPa
49
Flexural Strength
2mm/min
ISO 178
MPa
70
Flexural Modulus
2mm/min
ISO 178
MPa
1950
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
52
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
50
Rockwell Hardness
R-scale
ISO 2039-2
-
111
Izod Impact Strength (notched)
-30°C, 4mm
ISO 180 1A
KJ/m²
15