Niblend F817

Telefonische Beratung

+49 40 727702-0

- PC-ABS

alloy reinforced with 17 % of glass fibre

 

mso-fareast-font-family:"Times New Roman";color:red;mso-ansi-language:EN-GB;

mso-fareast-language:AR-SA;mso-bidi-language:AR-SA">- Grade for injection

moulding, characterized by very high heat resistance, high stiffness and easy

processing 

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
260°C / 5 kg
ASTM D1238
g/10min
10
Flame Behaviour
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,27
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,05
Moulding Shrinkage
parallel
-
%
0,2-0,4
Moulding Shrinkage
transversal
-
%
0,3-0,5
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
138
Ball Pressure Test
125°C
IEC 60695-10-2
-
Pass
Linear Expansion Coefficient
parallel
ISO 11359-2
cm/cm/°C
0,000030
Linear Expansion Coefficient
transversal
ISO 11359-2
cm/cm/°C
0,000080
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
5600
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
70
Elongation at Break
50 mm/min
ASTM D638
%
2
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
115
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
4800
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
90
Electrical
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,0085
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
35
Surface Resistivity
dry
IEC 60093
Ω
1016
Volume Resistivity
dry
IEC 60093
Ω • cm
1014