Niblend F17

Telefonische Beratung

+49 40 727702-0

PC-ABS alloy reinforced with 17% glass fibre, of high thermic resistance for the injection mouldibg

Of items needing high hardness and dimensional stability even at high temperatures.

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
260°C / 5 kg
ASTM D1238
g/10min
18
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,2
Moulding Shrinkage
parallel
-
%
0,4 – 0,8
Physical
Density
23°C
ASTM D792
g/cm³
1,23
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
123
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
115
Coef. Dilatazione Termica Lineare
23/55 °C
ISO 11359-2
10-5 K-1
4
Mechanical
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
70
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
100
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
5000
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
50
Rockwell Hardness
ASTM D785
R-scale
118
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
70
Elongation
50 mm/min
ASTM D638
%
3
Electrical
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
25
Relative Permettivity
1 Mhz = secco
IEC 60250
-
2,9
Dissipation Factor
1 Mhz = secco
IEC 60250
-
0,05
Surface Resistivity
secco
IEC 60093
Ω
1015
Volume Resistivity
secco
IEC 60093
Ω • cm
1015