Niblend S65F UV Nero905

Telefonische Beratung

+49 40 727702-0

PC-ABS alloy characterized by good heat resistance, good flow, and easy processing. Grade for injection moulding, particularly indicated for automotive industry.

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
260°C / 5 kg
ASTM D1238
g/10min
20
Flame Behaviour
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,12
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,2
Moulding Shrinkage
parallel
-
%
0,5-0,8
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
123
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
110
Coef. Dilatazione Termica Lineare
23/55 °C
ISO 11359-2
10-5 K-1
8
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-12
°C
650
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
50
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
80
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2300
Rockwell Hardness
23°C
ASTM D785
M-scale
116
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
550
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
150
Elongation
50 mm/min
ASTM D638
%
>50
Tensile Modulus
50 mm/min
ASTM D638
MPa
2350
Electrical
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
25
Relative Permettivity
1 Mhz = secco
IEC 60250
-
2,9
Dissipation Factor
1 Mhz = secco
IEC 60250
-
0,05
Surface Resistivity
secco
IEC 60093
Ω
1015
Volume Resistivity
secco
IEC 60093
Ω • cm
1015