Niblend S65/M

Telefonische Beratung

+49 40 727702-0

PC-ABS alloy of medium thermic resistence for the extrusion of profiles used by the automotive industry

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
260°C / 5 kg
ASTM D1238
g/10min
9
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,12
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,2
Moulding Shrinkage
parallel
-
%
0,5-0,8
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
115
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
110
Coef. Dilatazione Termica Lineare
23/55 °C
ISO 11359-2
10-5 K-1
9
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
40
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
60
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
1700
Rockwell Hardness
ASTM D785
R-scale
110
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
350
Izod Notched Impact Strength
-20°C/3,2 mm
ASTM D256
J/m
150
Elongation
50 mm/min
ASTM D638
%
50
Electrical
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
25
Relative Permettivity
1 Mhz = secco
IEC 60250
-
2,9
Dissipation Factor
1 Mhz = secco
IEC 60250
-
0,05
Surface Resistivity
secco
IEC 60093
Ω
1015
Volume Resistivity
secco
IEC 60093
Ω • cm
1015