Niplene F2T4 AGR HF

Telefonische Beratung

+49 40 727702-0

- Polypropylene homopolymer reinforced with 10% of glass fibre (chemically bounded) and 20% of

talcum.

- Grade developed for injection moulding of complex item, characterized by good fluidity, good

balance of mechanical properties and low warpage.

- Grade available also with improved heat stabilisation (SC)

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
13
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,13
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,13
Moulding Shrinkage
parallel
-
%
0,3-0,9
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
120
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
135
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
5
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
56
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
90
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
4250
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
60
Rockwell Hardness
ASTM D785
R-scale
109
Elongation
50 mm/min
ASTM D638
%
3,4
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
2,7
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,001
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60
Surface Resistivity
dry
IEC 60093
Ω
1015
Volume Resistivity
dry
IEC 60093
Ω • cm
1015