Telefonische Beratung

+49 40 727702-0

Polypropilene homopolymer reinforced with 50% of glass fibres, with chemical boud between fibres and the polymeric matrix, for the moulding of items that needs an exceptional stiffness.

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
2,5
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,33
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,1
Moulding Shrinkage
parallel
-
%
0,2-0,4
Moulding Shrinkage
transversal
-
%
0,3-0,6
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
146
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
158
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
3
Mechanical
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
110
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
180
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
10500
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
130
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
90
Rockwell Hardness
ASTM D785
R-scale
115
Elongation
50 mm/min
ASTM D638
%
2,5
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
2,7
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,001
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60
Surface Resistivity
dry
IEC 60093
Ω
1014
Volume Resistivity
dry
IEC 60093
Ω • cm
1015