Niplene SV30

Telefonische Beratung

+49 40 727702-0

- Polypropylene homopolymer reinforced with 30% of glass beads.

- Grade developed for injection molding of items characterized by good aesthetics and dimensional

stability

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
12
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,12
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,1
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
95
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
37
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2000
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
35
Elongation
5mm/min
ASTM D638
%
>50
Tensile Modulus
5 mm/min
ASTM D638
MPa
2500
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
22