Niplene T20/C E

Telefonische Beratung

+49 40 727702-0

- Polypropylene copolymer, filled with 20 % of talcum for extrusion of sheets and profiles and for

extrusion blow moulding.

- Grade characterized by very low MFI and good balance impact/stiffness.

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
1,5
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,05
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
85
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
70
Heat Distortion Temperature H.D.T
0,455 MPa
ASTM D648
°C
118
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
37
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2100
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
150
Rockwell Hardness
ASTM D785
R-scale
101
Elongation
5mm/min
ASTM D638
%
>40
Tensile Modulus
5 mm/min
ASTM D638
MPa
2750
Tensile Stress at Yield
5 mm/min
ASTM D638
MPa
23
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
2,7
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,001
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60
Surface Resistivity
dry
IEC 60093
Ω
1014
Volume Resistivity
dry
IEC 60093
Ω • cm
1015