Niplene T40 HF

Telefonische Beratung

+49 40 727702-0

- Polypropylene homopolymer, filled with 40 % of talcum for injection moulding.

- Grade characterized by high fluidity, good processability high stiffness and good dimensional stability

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
22
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Moulding Shrinkage
parallel
-
%
0,4-0,8
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
108
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
90
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
30
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
50
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
4000
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
30
Rockwell Hardness
ASTM D785
R-scale
106
Elongation
50 mm/min
ASTM D638
%
20
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
2,7
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,001
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60
Surface Resistivity
dry
IEC 60093
Ω
1014
Volume Resistivity
dry
IEC 60093
Ω • cm
1015