Niplene C30

Telefonische Beratung

+49 40 727702-0

Polypropylene homopolymer, filled with 30% calcium carbonate, for the injection moulding of items of medium hardness and good aesthetical surface.

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
10
Various
Density
ASTM D792
g/cm³
1,12
Moulding Shrinkage
parallel
-
%
0,8-1,4
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
110
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
65
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
20
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
45
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2800
Rockwell Hardness
ASTM D785
R-scale
105
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
30
Elongation
50 mm/min
ASTM D638
%
60