Niplene C50

Telefonische Beratung

+49 40 727702-0

Polypropylene homopolymer, filled with 50% calcium carbonate, for the injection moulding of Items of medium hardness and good aesthetical surface

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
8
Various
Density
ASTM D792
g/cm³
1,24
Moulding Shrinkage
parallel
-
%
0,7-1,2
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
115
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
70
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
20
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
45
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
3300
Rockwell Hardness
ASTM D785
R-scale
108
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
20
Elongation
50 mm/min
ASTM D638
%
30