Nipene F20 AGR

Telefonische Beratung

+49 40 727702-0

Polypropylene homopolymer, reinforced with 20% glass fibre chemically coupled to the polymeric matrix

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
4,5
Flame Behaviour
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Density
ASTM D792
g/cm³
1,05
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,2
Moulding Shrinkage
parallel
-
%
0,3-0,7
Moulding Shrinkage
transversal
-
%
0,4-1,0
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
138
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
152
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
4
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-12
°C
650
Mechanical
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
80
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
110
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
4500
Rockwell Hardness
ASTM D785
R-scale
113
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
110
Izod Notched Impact Strength
-20°C/3,2 mm
ASTM D256
J/m
70
Elongation
50 mm/min
ASTM D638
%
3,5
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
2,7
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60
Surface Resistivity
dry
IEC 60093
Ω
1014
Volume Resistivity
dry
IEC 60093
Ω • cm
1015