Niplene T20 FR V0

Telefonische Beratung

+49 40 727702-0

Polypropylene homopolymer, talc filled 20%, flame retardant with an UL 94 V0 at 3.2 mm rating

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
230 °C / 2,16 Kg
ASTM D1238
g/10min
9
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
960
UL 94 Rating
S=1.6 mm
UL 94
class
V2
UL 94 Rating
S=3.2 mm
UL 94
class
V0
Various
Density
ASTM D792
g/cm³
1,32
Humidity Content at Equilibrium
23°C / 50 % U.R.
ISO 62
%
0,3
Moulding Shrinkage
parallel
-
%
0,4-0,8
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
116
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
90
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
25
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
50
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
3400
Rockwell Hardness
ASTM D785
R-scale
86
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
30
Elongation
50 mm/min
ASTM D638
%
50