Niretan A EXL

Telefonische Beratung

+49 40 727702-0

 

Polyamide 66 of natural colour, with external additivation.

Easy flowing and fast processing.

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
750
UL 94 Rating
S=1.6 mm
UL 94
class
V2
UL 94 Rating
S=3.2 mm
UL 94
class
V2
Various
Moulding Shrinkage
parallel
-
%
1,2-2
Physical
Density
23°C
ASTM D792
g/cm³
1,14
Water Absorption
24h - 23°C
ASTM D570
%
9
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2,7
Cristalline Melting Temperature
DSC
-
°C
260
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
240
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
75
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
9
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
85/50
Elongation at Break
50 mm/min
ASTM D638
%
30/>50
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
110/60
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2900/1200
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
60/150
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
40/70
Rockwell Hardness
23°C
ASTM D785
R-scale
110/95
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
3,5/4,0
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,02/0,1
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
30/25
Surface Resistivity
dry
IEC 60093
Ω
1014/1013
Volume Resistivity
dry
IEC 60093
Ω • cm
1015/1012