Niretan A F30 AE/V0

Telefonische Beratung

+49 40 727702-0

Polyamide 66 reinforced with 30% of glass fibre, flame retarded. U.L. 94 rating: V0 at 1,6 mm

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
960
UL 94 Rating
S=1.6 mm
UL 94
class
V0
UL 94 Rating
S=3.2 mm
UL 94
class
V0
Various
Moulding Shrinkage
parallel
-
%
0,3-0,7
Physical
Density
23°C
ASTM D792
g/cm³
1,56
Water Absorption
24h - 23°C
ASTM D570
%
6
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2
Cristalline Melting Temperature
DSC
-
°C
260
Thermal
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
245
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
4
Mechanical
Tensile Stress at Yield
50 mm/min.
ASTM D638
MPa
130/80
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
160/110
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
9500/6000
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
70/90
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
50/70
Rockwell Hardness
ASTM D785
R-scale
115/90
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
3,5/4,0
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,02/0,1
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
30/35
Surface Resistivity
dry
IEC 60093
Ω
1014/1013
Volume Resistivity
dry
IEC 60093
Ω • cm
1015/1012