Polyamide 66 reinforced with 30% of Talcum, for injection moulding.

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Moulding Shrinkage
parallel
-
%
0,7-1,2
Physical
Density
23°C
ASTM D792
g/cm³
1,36
Water Absorption
24h - 23°C
ASTM D570
%
5
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2
Cristalline Melting Temperature
DSC
-
°C
260
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
210
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
80
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
6
Heat Distortion Temperature H.D.T
0,455 MPa
ASTM D648
°C
220
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
105
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
5400
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
50
Elongation
5mm/min
ASTM D638
%
5
Tensile Modulus
5 mm/min
ASTM D638
MPa
6200
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
60