Polyamide 6, reinforced with 15 % of glass fibre, impact modified, for injection moulding

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Moulding Shrinkage
parallel
-
%
0,5/1,0
Physical
Density
23°C
ASTM D792
g/cm³
1,21
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2,5
Cristalline Melting Temperature
DSC
-
°C
220
Thermal
Vicat Softening Temperature
49N / 120°C/h
ASTM D 1525
°C
205
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
175
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
6
Mechanical
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
100
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
145
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
4500
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
90
Rockwell Hardness
ASTM D785
R-scale
100
Elongation
50 mm/min
ASTM D638
%
3,7
Electrical
Surface Resistivity
dry
IEC 60093
Ω
1014/1013
Volume Resistivity
dry
IEC 60093
Ω • cm
1015/1012