Niretan B F30 M2

Telefonische Beratung

+49 40 727702-0

Polyamide 6 reinforced with 30% of glass fibre, impact modified, for injection moulding.

Material available also with heat stabilisation. (SC)

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Moulding Shrinkage
parallel
-
%
0,25/0,6
Physical
Density
23°C
ASTM D792
g/cm³
1,3
Water Absorption
24h - 23°C
ASTM D570
%
6,6
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2,1
Cristalline Melting Temperature
DSC
-
°C
220
Thermal
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
200
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
4
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
175/110
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
6600/4200
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
230/380
Elongation
50 mm/min
ASTM D638
%
4/8,5
Tensile Modulus
5 mm/min
ASTM D638
MPa
8000/5000
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
135/90
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
3,8/4,2
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,02/0,12
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
34/24
Surface Resistivity
dry
IEC 60093
Ω
1014/1013
Volume Resistivity
dry
IEC 60093
Ω • cm
1015/1012