Niretan B SV25 AE/V0

Telefonische Beratung

+49 40 727702-0

 

Polyamide 6,filled with 25% of glass beads, flame retarded of U.L.94 V0 1,6 mm rating, for injection moulding.

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
960
UL 94 Rating
S=1.6 mm
UL 94
class
V0
UL 94 Rating
S=3.2 mm
UL 94
class
V0
Various
Moulding Shrinkage
parallel
-
%
0,5-1,2
Physical
Density
23°C
ASTM D792
g/cm³
1,49
Water Absorption
24h - 23°C
ASTM D570
%
6
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2,5
Cristalline Melting Temperature
DSC
-
°C
220
Thermal
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
65
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
8
Mechanical
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
60-45
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
80
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
3800/1300
Izod Notched Impact Strength
23°C/3mm
ASTM D256
J/m
40/70
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
30/40
Rockwell Hardness
23°C
ASTM D785
R-scale
95
Elongation
50 mm/min
ASTM D638
%
4-10
Electrical
Relative Permettivity
1 Mhz – dry
IEC 60250
-
3,5/4,0
Dissipation Factor
1 Mhz – dry
IEC 60250
-
0,02/0,1
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
30/25
Surface Resistivity
dry
IEC 60093
Ω
1014/1013
Volume Resistivity
dry
IEC 60093
Ω • cm
1015/1012