Polyamide 6 flame retardant as per UL 94 V0 at 1.6 mm rating

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
960
UL 94 Rating
S=1.6 mm
UL 94
class
V0
UL 94 Rating
S=3.2 mm
UL 94
class
V0
Physical
Density
23°C
ASTM D792
g/cm³
1,16
Water Absorption
24h - 23°C
ASTM D570
%
9/10
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
25/3,4
Cristalline Melting Temperature
DSC
-
°C
215/220
Thermal
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
70
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
7,5
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
120/60
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
2800/800
Rockwell Hardness
ASTM D785
R-scale
120/102
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
50/600
Izod Notched Impact Strength
-20°C/3mm
ASTM D256
J/m
45/500
Elongation
5mm/min
ASTM D638
%
>60/>200
Tensile Stress at Break
5 mm/min
ASTM D638
MPa
60/30
Tensile Stress at Yield
5 mm/min
ASTM D638
MPa
80/40
Electrical
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
60/40
Relative Permettivity
1 Mhz = secco
IEC 60250
-
3,8
Dissipation Factor
1 Mhz = secco
IEC 60250
-
0,03
Surface Resistivity
secco
IEC 60093
Ω
1012/1010
Volume Resistivity
secco
IEC 60093
Ω • cm
1015/1011