Niretan B CF1515

Telefonische Beratung

+49 40 727702-0

Poliamide 6 rinforced with a mix glass fibre and mineral filler, for the injection moulding of parts

That need good isotropic properties.

Properties
Test condition
Method
Unit
Value
Flame Behaviour
Glow Wire Temperature (G.W.T)
S=2.0 mm
IEC 695-2-1
°C
650
UL 94 Rating
S=1.6 mm
UL 94
class
HB
UL 94 Rating
S=3.2 mm
UL 94
class
HB
Various
Moulding Shrinkage
parallel
-
%
0,6/1,2
Physical
Density
23°C
ASTM D792
g/cm³
1,36
Water Absorption
24h - 23°C
ASTM D570
%
6-7
Humidity Absorption from Atmosphere
23°C – 50% HR
ASTM D570
%
2
Cristalline Melting Temperature
DSC
-
°C
220
Thermal
Heat Distortion Temperature H.D.T
1.82 MPa
ASTM D648
°C
60
Linear Expansion Coefficient
23°C/55°C
ISO 11359-2
10-5 K-1
10
Mechanical
Flexural Maximum Stress
1,3 mm/min
ASTM D790
MPa
160/90
Flexural Elastic Modulus
1,3 mm/min
ASTM D790
MPa
6000/2600
Rockwell Hardness
ASTM D785
R-scale
120/80
Izod Notched Impact Strength
23°C/3,2 mm
ASTM D256
J/m
40/60
Izod Notched Impact Strength
-20°C/3,2 mm
ASTM D256
J/m
30/30
Elongation
5mm/min
ASTM D638
%
4/10
Tensile Stress at Yield
5 mm/min
ASTM D638
MPa
120/60
Electrical
Dielectric Strength
S=1 mm
IEC 60243-1
KV/mm
30/25
Relative Permettivity
1 Mhz = secco
IEC 60250
-
3,5/4,0
Dissipation Factor
1 Mhz = secco
IEC 60250
-
0,02/0,1
Surface Resistivity
secco
IEC 60093
Ω
1014/1013
Volume Resistivity
secco
IEC 60093
Ω • cm
1015/1012