Poketone M930A

Telefonische Beratung

+49 40 727702-0

- High flow base resin (Natural)

Properties
Test condition
Method
Unit
Value
Rheological
Melt Flow Index
240°C/2,16kg
ASTM D1238
g/10min
200
Impact
Notched Charpy Impact Strength
23°C
ISO 179/1eA
KJ/m²
7
Flammability
Flammability
t = 0,8mm
UL94
Class
HB
Physical
Specific Gravity
ASTM D792
g/cm³
1.24
Water Absorbtion
23°C, 50%RH
ASTM D570
%
0.5
Mold Shrinkage
3T, MD/TD
ASTM D955
%
1.8/1.7
Thermal
Melting Temperature
ASTM D3418
°C
222
Heat Deflection Temperature
18,6kg/cm²
ASTM D648
°C
105
Mechanical
Tensile Strength at Yield
23°C
ASTM D638
MPa
62
Tensile Strain at Break
23°C
ASTM D638
%
130
Flexural Strength
23°C
ASTM D790
MPa
60
Flexural Modulus
23°C
ASTM D790
MPa
1600