Starex BF-0677HF

Telefonische Beratung

+49 40 727702-0

MABS, hochglänzend, kratzfest

Properties
Test condition
Method
Unit
Value
Flammability
Flammability
HB
UL94
mm
1.5,3.0
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,13
Melt Flow Index
220°C, 10kg
ISO 1133
g/10min
19
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,4
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,5
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
76
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
88
Vicat Softening Temperature
B/50
ISO R 306
°C
95
Vicat Softening Temperature
B/120
ISO R 306
°C
98
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
53
Tensile Strain at Break
50mm/min
ISO 527
%
20
Tensile Modulus
50mm/min
ISO 527
MPa
2600
Tensile Strength at Break
50mm/min
ISO 527
MPa
38
Flexural Strength
2mm/min
ISO 178
MPa
80
Flexural Modulus
2mm/min
ISO 178
MPa
2600
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
10
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
10
Rockwell Hardness
R-scale
ISO 2039-2
-
116
Pencil Hardness
500g
JIS K 5401
-
H