Starex HG-0760AT

Telefonische Beratung

+49 40 727702-0

ABS hochglänzend, leichtfließend, temporär antistatisch

Properties
Test condition
Method
Unit
Value
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,04
Melt Flow Index
200°C, 5kg
ISO 1133
g/10min
3,5
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,34~0,42
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,36~0,45
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
82
Vicat Softening Temperature
B/50
ISO R 306
°C
94
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
42
Tensile Strain at Break
50mm/min
ISO 527
%
20
Tensile Modulus
50mm/min
ISO 527
MPa
2400
Tensile Strength at Break
50mm/min
ISO 527
MPa
34
Flexural Strength
2mm/min
ISO 178
MPa
63
Flexural Modulus
2mm/min
ISO 178
MPa
2200
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
16
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
18
Rockwell Hardness
R-scale
ISO 2039-2
-
109