Starex MP-0670

Telefonische Beratung

+49 40 727702-0

ABS Galvano-Type

Properties
Test condition
Method
Unit
Value
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,04
Melt Flow Index
200°C, 5kg
ISO 1133
g/10min
2,3
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,5
Water Absorption
23°C
ISO 62
%
0,3
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
80
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
93
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
96
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
100
Vicat Softening Temperature
B/50
ISO R 306
°C
100
Vicat Softening Temperature
B/120
ISO R 306
°C
101
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
51
Tensile Strain at Break
50mm/min
ISO 527
%
3
Tensile Modulus
50mm/min
ISO 527
MPa
2350
Tensile Strength at Break
50mm/min
ISO 527
MPa
37
Flexural Strength
2mm/min
ISO 178
MPa
72
Flexural Modulus
2mm/min
ISO 178
MPa
2350
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
25
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
25
Rockwell Hardness
R-scale
ISO 2039-2
-
106
Izod Impact Strength (notched)
-30°C, 4mm
ISO 180 1A
KJ/m²
8