Starex SR-0300

Telefonische Beratung

+49 40 727702-0

ABS gute Wärmeformbeständigkeit, emissionsreduziert

Properties
Test condition
Method
Unit
Value
Physical
Specific Gravity
Natural or Representative Color
ISO 1183
-
1,05
Melt Flow Index
220°C, 10kg
ISO 1133
g/10min
13
Mold Shrinkage (MD)
Flow at 3.2mm(MD)
ISO 2577
%
0,38-0,46
Mold Shrinkage (TD)
X-Flow at 3.2mm(TD)
ISO 2577
%
0,40-0,49
Thermal
Heat Deflection Temperature (unannealed)
1.8 MPa, 4.0mm
ISO 75-2
°C
76
Heat Deflection Temperature (unannealed)
0.45 MPa, 4.0mm
ISO 75-2
°C
95
Heat Deflection Temperature (annealing)
1.8 MPa, 4.0mm
ISO 75-2
°C
97
Heat Deflection Temperature (annealing)
0.45 MPa, 4.0mm
ISO 75-2
°C
102
Vicat Softening Temperature
B/50
ISO R 306
°C
102
Vicat Softening Temperature
B/120
ISO R 306
°C
105
Mechanical
Tensile Strength at Yield
50mm/min
ISO 527
MPa
48
Tensile Strain at Break
50mm/min
ISO 527
%
22
Tensile Modulus
50mm/min
ISO 527
MPa
2400
Tensile Strength at Break
50mm/min
ISO 527
MPa
35
Flexural Strength
2mm/min
ISO 178
MPa
76
Flexural Modulus
2mm/min
ISO 178
MPa
2500
Izod Impact Strength (notched)
at 23°C, 4mm
ISO 180 1A
KJ/m²
22
Charpy Impact Strength (V-notched)
23°C, 4mm
ISO 179 1eA
KJ/m²
25
Rockwell Hardness
R-scale
ISO 2039-2
-
110