Niplene T20 FR V0
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
<font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"> </font></font></font>
Polypropylene homopolymer, talc filled 20%, flame retardant with an UL 94 V0 at 3.2 mm rating
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Rheological | Melt Flow Index | 230 °C / 2,16 Kg | ASTM D1238 | g/10min | 9 |
Mechanical | Tensile Stress at Yield | 50 mm/min. | ASTM D638 | MPa | 25 |
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 50 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 3400 |
Mechanical | Rockwell Hardness | ASTM D785 | R-scale | 86 | |
Mechanical | Izod Notched Impact Strength | 23°C/3,2 mm | ASTM D256 | J/m | 30 |
Mechanical | Elongation | 50 mm/min | ASTM D638 | % | 50 |
Thermal | Vicat Softening Temperature | 49N / 120°C/h | ASTM D 1525 | °C | 116 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 90 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 960 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | V2 |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | V0 |
Various | Density | ASTM D792 | g/cm³ | 1,32 | |
Various | Humidity Content at Equilibrium | 23°C / 50 % U.R. | ISO 62 | % | 0,3 |
Various | Moulding Shrinkage | parallel | - | % | 0,4-0,8 |